TZS® Zirconium Silciate grinding beads

Page view:
Name

TZS® Zirconium Silciate grinding beads

没有此类产品
Product description

Tecera International

Zirconium Silciate grinding beads

Application:

Type

Application

TZS320®

1. Non-metallic minerals like Calcium Carbonate, kaolin clay, zirconium silicate, TiO2 and    other minerals;
2.Metallic minerals like copper, silver, nickel, gold, zinc etc;
3. White pigments, coatings, paints, inks etc;
4.Recommend to be used in stirred mill and ball mill.

TZS360®

1. Non-metallic minerals like Zirconium Silicate, Calcium Carbonate, kaolin clay;
2. Ceramic glazes and frits;
3. Coatings, paints, inks etc;
4. Metallic minerals like copper, silver, nickel, gold, zinc etc;
5. Recommend to be used in stirred mill and ball mill.

TZS400®

1. Non-metallic minerals like Zirconium Silicate,GCC, kaolin clay;
2. Engineering Ceramics.
3. Coatings, paints, inks etc;
4. Metallic minerals like copper, silver, nickel, gold, zinc etc;
5. Metal finishing and polishing.

TZS420®

1.Non-metallic minerals like Calcium Carbonate, kaolin clay, zirconium silicate, TiO2 and    other minerals;
2. Dielectric materials, piezoelectric materials, capacitor;
3. Ceramic glazes and frits;
4. Coatings, paints, inks etc;
5. Metallic minerals like copper, silver, nickel, gold, zinc etc;
6. Recommend to be used in stirred mill and ball mill.

Specification  

Specification

TZS 320®

 TZS360®

TZS400®  

TZS420®

Chemical
composition

ZrO2 Al2O3   SiO2  
Other

ZrO2   Al2O3   SiO2  
Other

ZrO2   Al2O3   SiO2 
Other

ZrO2   Al2O3   SiO2 
Other

Density

>3.25

3.60~3.70

>4.0

 4.20min

Packing 
Density

>1.85


2.20~2.35

>2.35

2.85min

Hardness
(Mohs)

8  

8  

> 8

8min

Roundness

>90%

>90%

>90%

>90%

Size

0.2 ~ 12mm  ,

0.2 ~ 12mm,

0.4 ~ 13mm,.

0.2 ~ 12mm,

Color

White

White

off-white

White

 

■Packaging:

25kg net in PP-bag or big bag of 500 or 1000kg net. 20-24MT/20'FCL.

■Key benefits:

·Very High grinding efficiency for superfine grinding.

·Fine chemical stability & contamination-free to the grinded material.

·Extremely low wear rate .

·Excellent combination of toughness and hardness .

·Technical support provided to optimize milling conditions .

Wear Loss Testing

Grinding Beads

Size
(mm)

Beads loading
quantity/g

Weight of beading after grinding/g

Wear Loss/g

  Wear Loss 
Rate /%

Alumina Grinding Beas
(China)

8

500

498.6

1.4

0.28%

TZS400 ceramic beads

8-10

500

499.7

0.3

0.06%

Testing Method:Ceramic beads loading quantity 500g, water loading quantity150g,grinding time 1 hour,volume of jar mill : 500ml.

■Conclusion: 

The wear loss rate of alumina ceramic beads is about 4.6 times higher than TZS400 zirconium silicate grinding beads.

 